Fabric-prepreg type 926
Products from remaining stock : Carbon fibre prepregs with epoxy resin 913 C
With epoxy resin 913 C: hardening at 125°C, at least 60 min,
Storage time: 30 days at room temperature, 360 days at -18°C
| Fibres | Tenax HTA/HTS or Toray 300J |
| Yarn | 6K |
| Weave | satin 1/4 |
| Thickness of the fabric | 0,350 mm |
| Standard width of rolls | 1270 mm |
| Areal weight of the prepreg | 570 g/m² in case of 35% resin |
| 620 g/m² in case of 40% resin | |
| Areal weight of the fabric | 370 g/m² |
| In warp direction | In fill direction | |
| Tensile strength | 900 MPa | 800 MPa |
| Tensile modulus of elasticity |
70 GPa | 67 GPa |
| Compressive strength | 760 MPa | 680 MPa |
with epoxy resins 6376, 977, M21, 8552
Fabric-Prepreg Type 926
With epoxy resins 6376, 977: hardening at 180°C, at least 120 min,
Storage time: 21 days at room temperature, 180 days at -18°C
| Fibres | Tenax HTA/HTS oder Toray 300J |
| Yarn | 6K |
| Weave | satin 1/4 |
| Thickness of the fabric | 0,350 mm |
| Standard width of rolls | 1270 mm |
| Areal weight of the prepreg | 570 g/m² in case of 35% resin |
| 620 g/m² in case of 40% resin | |
| Areal weight of the fabric | 370 g/m² |
| In warp direction | In fill direction (90°) | |
| Tensile strength | 900 MPa | 800 MPa |
| Tensile modulus of elasticity |
70 GPa | 67 GPa |
| Compressive strength | 760 MPa | 680 MPa |