	Unidirectional Prepreg With epoxy resins 6376, 977, M21, 8552: hardening at 180°C, at least 120 min, Storage time: 21 days at room temperature, 180 days at -18°C Fibres Tenax HTA/HTS or Toray 300J Yarn 12K-rovings arranged in parallel Standard width of rolls 1270 mm Thickness of layers 0,125 mm 0,250 mm Areal weight of the prepreg 203 g/m² at 35% resin 406 g/m² at 35% resin 220 g/m² at 40% resin 440 g/m² at 40% resin Areal weight of the fibres 132 g/mē 264 g/mē   Longitudinal along fibre Perpendicular to fibre Tensile strength 1950 MPa 75 MPa Tensile modulus of elasticity 130 MPa 9100 MPa Compressive strength 1500 MPa 230 MPa