Fabric-Prepreg Type 926
With epoxy resins 6376, 977: hardening at 180°C, at
least 120 min,
Storage time: 21 days at room temperature, 180 days at -18°C
Fibres
|
Tenax HTA/HTS oder Toray 300J |
Yarn
|
6K |
Weave
|
satin 1/4 |
Thickness of the fabric
|
0,350 mm |
Standard width of rolls
|
1270 mm |
Areal weight of the prepreg
|
570 g/mē in case of 35% resin |
| 620 g/mē in case of 40% resin |
| Areal weight of the fabric |
370 g/mē |
| |
In warp direction |
In fill direction (90°) |
| Tensile strength |
900 MPa |
800 MPa |
Tensile modulus
of elasticity |
70 GPa |
67 GPa |
| Compressive strength |
760 MPa |
680 MPa |
|
|