Carbon Fibre Fabric

RTM-resin-injection-process Injectex G 926 / EFP
Fibres HTA
Primer 5131
Yarn 6K
Weave satin 1/4
Epoxy resin-binder 5 % by weight
(incl. primer)
Glass threads ./.
Thickness of the fabric 0,350 mm
Standard width of rolls 1270 mm
Areal weight of the fabric 395 g/mē (incl. binder)
Areal weight of the fibres 370 g/mē

Properties after curing with epoxy resin RTM 6:

  In warp direction In fill direction (90°)
Tensile strength 870 MPa 830 MPa
Tensile modulus
of elasticity		 68 GPa 68 GPa
Compressive strength 715 MPa 730 MPa

- in addition fabrics with the types of weave plain, twill
(areal weight: 93 g/m² up to 600 g/m²), available according
to stock, especially remnants with kinks and faults,
sometimes in rolls, 300 - 1450 mm widths.